Unalloyed iron samples were sintered in DC plasma formed by hydrogen and argon using the following electrode geometries: anode with and without metallic protector. Water atomized iron powder was compacted at 600 MPa and sintered in plasma atmosphere in order to investigate respectively the microstructure changes on the surface and in the bulk of the samples with temperatures varying from 740 to 1100 ºC. The samples when sintered on anode with metallic protector geometry presented deposition of manganese and sulphur found out in the materials used to construct the electrodes. With regard to microstructural characterization, the samples showed large and irregular grains different from those processed in resistance furnace.
Biografia do Autor
Jorge Magner Lourenço, Instituto Federal de Educação, Ciências e Tecnologia do RN
Bacharel em engenharia mecânica pela UFRN, mestrado em engenharia mecânica pela mesma instituição e doutorado em ciênicas e engenharia de materias pela UFSC. Trabalhou com sinterização a plasma.
Henrique César Pavanati, Universidade Federal de Santa Catarina
Departamento de Engenharia Mecânica -
Laboratório de Materiais - LabMat
Ana Maria Maliska, Universidade Federal de Santa Catarina
Departamento de Engenharia Mecânica -
Laboratório de Materiais - LabMat
Aloísio Nelmo Klein, Universidade Federal de Santa Catarina
Departamento de Engenharia Mecânica -
Laboratório de Materiais - LabMat