Samples of PEEK – poly(ether-ether-ketone) were coated with titanium through flame thermal spray process, using nitrogen or argon as carrier gas. The coatings were characterized by optical and scanning electronic microscope, energy dispersive x-ray detector (EDS) and diffraction x-ray (DRX). Tribological tests were performed on the Ti coatings and an abrasive wear was identified for both samples. The bioactivity of the as-prepared coating surface samples was evaluated in in-vitro tests by immersion of the samples in simulated body fluid (SBF) for different periods of time, up to 23 days. The coated specimens were analyzed by SEM and EDS and revealed that a layer containing Ca and P was deposited upon immersing the samples in SBF, suggesting that compounds similar to bones (apatite) were formed and therefore, the materials have a potential use in implants for consolidating bone fractures.
Biografia do Autor
Andreza Maria Ribeiro, Universidade Federal do Paraná
Possui o título de Doutorado Europeu em Tecnologia Farmacêutica concedido pela Universidade de Coimbra em Portugal, realizou 3 anos da parte experimental do doutorado na Universidade de Santiago de Compostela na Espanha. Possui especialização e mestrado em Tecnologia Farmacêutica realizado na Faculdade de Farmácia da Universidade do Porto em Portugal. Possui experiência na área das Ciências da Saúde (Farmácia) com ênfase na Tecnologia Farmacêutica. Amplo conhecimento na pesquisa e desenvolvimento de diferentes formas farmacêuticas com foco em formas farmacêuticas de liberação modificadas, solubilização de fármacos, síntese de biopolímeros, novas tecnologias como a biomimética e "molecular imprinting", pré-formulações, nanotecnologia, análise quantitativa e qualitativa. Atualmente trabalha com polimeros biodegradáveis na área do desenvolvimento de revestimentos para implantes.